LaAlO₃ single crystal has a lattice constant (a=3.790 Å) which fits high Tc superconductive material (such as YBCO: 3.86 Å) very well, proper dielectric constant and low dielectric loss in microwave band, so it is suitable for high Tc microwave electronic devices (for example high Tc superconductive filter in mobile communication). It is grown by Czechrolsky method, possible to get large size (2”and 3” in diameter) and high quality crystal and substrate. It is an important substrate that has been applied in communication industry.

Crystal structure	Triclinic 3 m Peroviskite
Cell parameter	a =12.376Å α=90°5''''  Pseudo-cubic
Melting Point	2373°K
Density	6.52 g/cm3
Specific Heat	0.427J/g∙k (298°K)
Thermal conductivity	11.6W/m∙k (300°K)
Theramal expansion	9.18x10-6k-1 (940°K)
Dielectric constant (εr)	24(295°K) 23.7(80°K) (18-35GHz)
Dielectric loss (tgδ)	6x10-6(80°K) Microwave
Hardness (Mohs)	6.5
Growth Method	Czockralski

Standard Size: Ф3″,Ф2″,Ф1″, 20x20, 10x10, 10x5, 10x3mm or customer design.
Thickness: 0.5mm,1.0mm.
Thickness tolerance:±0.02mm or 0.005mm for special order;
Polish: one or two sides
Orientation: <100> <110> <111>
Orientation accuracy: ±0.5°
Edge Orientation accuracy: 2° (or 1°for special order)
Cut with special tilt angle: available(tilt angle:1°-45°)
Micro roughness Ra:  ≤5Å(5μm×5μm)